Unsaturated polyester resin

1: Hand lay-up General purpose

Code	Type	25?  Pa.s Viscosity	Min gel time	% Non-Volatile	Mpa Tensile strength	% Elongation	Mpa Flexural Strength	HDT	Application
TK-806	PA	0.60-1.15	9.1-18.1	64-70	76	2.0	120	72	Flexibility,high impact strength
TK-189	PA	0.25-0.45	10-22	59-65	60	4.0	100	57	Water resistance, for boat.CCS
TK-191	PA	0.25-0.45	9-17	61-67	55	1.8	110	66	Translucent, general FRP purpose
TK-191RS	PA	0.25-0.45	9-17	61-67	60	3.5	114	70	For FRP product, general purpose
TK-195	PA	0.12-0.22	30-54	58-64	55	1.2	115	54	For Tramsparency FRP product
TK-196	PA	0.60-1.20	9.1-18.9	64-70	76	2.0	120	72	Flexibility, high strength, CCS
TK-198	PA	0.45-0.80	11-20	60-67	60	1.4	115	100	High thermal properties, high HDT, high strength
TK-580	IPA	0.40-0.70	10-20	66-70	15	68	10	67	Flexibilizer or flexible resin, with other resins
TK-1032	PA	0.25-0.65	15-23	15-23	60	2.0	105	67	Good mechanical property, for bus,boat, CCS approval
TK-22	PA	0.34-0.38	16-22	16-22	62	2.3	108	65	Pre-promoted, thixotropy and low shrinkage
TK-2068	PA	0.20-0.40	11-25	11-25	58	1.5	110	100	Hot water resistance and high HDT,for bathtub
TK-10070	PA	0.30-0.34	8-18	8-18	65	2.0	115	68	Low viscosity, rapid wetting reinforcement for high strength FRP products.

2:Flame retardant




Code	Type	25  Pa.s Viscosity	Min gel time	% Non -Volatile	Mpa Tensile strength	% Elongation	Mpa Flexural Strength	Application
TK-107L	reactive	0.35-0.65	16-30	62-68	320		256	Flame retardant, for boat, ccs OI=32
TK-107M	reactive	0.35-0.65	15-30	64-70	340		336	Flame retardant, for boat, OI=34
TK-108	reactive	0.25-0.55	30-60	62-69	288		348	Flame retardant, transparency, OI=32
TK-480	reactive	0.30-0.40	11-24	65-71	260		280	High flame retardant and low smoke emission, for railway FRP  OI=36
TK-107XHA	reactive	0.30-0.45	11.5-23.5	65-71	250		260	High flame retardant and high strength, good processability, Ccs approved, OI=36
TK-802	filled	0.60-1.20	11-22		202		225	Flame retardant,filled type, general purpose FRP, OI=30
TK-802P	filled	0.60-1.20	15-25		210		232	Pro-promoted, flame retardant, filled type, general purpose FRP OI=30
TK-V1053	filled	0.40-0.80	10-20		261		232	No-halogen,high flame retardant, low smoke emission, for railway FRP, OI=37

3:Chemical resistance

Code	Type	25  Pa.s Viscosity	Min gel time	% Non -Volatile	Mpa Tensile strength	% Elongation	Mpa Flexural Strength	HDT	Application
TK-197	bisphenol	0.48-0.98	13-27	46-53	55	1.5	100	115	Good alkali resistance, for FRP etc
TK-199	IPA	0.40-0.80	12-22	58-64	55	1.5	95	120	High HDT or heat resistance, chemical resistance, for FRP pipe etc

4: Food grade

TK-196SP	PA	0.65-1.15	9.1-18.9	64-70	76	2.3	120	73	Food grade, lining resin, CNH approval
TK-198SP	PA	0.45-0.80	11-20	60-67	60	1.4	115	100	Food grade, CNH approval

5. Spray up

TK-1032	PA	0.14-0.54	15-30	58-64	60	2.0	120	65	Thixotropy, pre-promoted, for hand lay-up or spray up allocation to fabricate all kinds of FRP products, CCS approval
TK-1021	PA	0.38-0.54	12-22	58-64	58	1.6	110	66	Thixotropy, pre-promoted, for hand lay-up or spray up allocation to fabricate FRP products

6. For boat

TK-196	PA	0.60-1.20	9.1-18.9	64-70	76	2.0	120	72	General purpose, CCS approval
TK-107M	Reactive	0.58-0.65	15-30	64-70	50	1.5	85	70	Flame retardant, CCS approval
TK-1032TP	PA	0.45-0.55	10-20	58-64	60	2.0	100	65	Low shrinkage, thixotropy pre-promoted, CCS approval
TK-189	PA	0.25-0.45	10.5-21.5	59-65	60	4.0	100	57	Water and chemical resistance, high elongation, CCS approval

7. Button

Code	Type	25?  Pa.s Viscosity	Min gel time	% Non-Volatile	Mpa Tensile strength	% Elongation	Mpa Flexural Strength	HDT	Application
TK-253	IPA	0.90-1.05	5-10	64-70	60	3.0	100	70	High impact strength
TK-2001	PA	0.75-1.05	8-12	64-70	48	1.5	98	53	Good gloss and transparency
TK-20750	IPA	0.90-1.05	15-20	64-70	58	3.4	90	55	High impact strength

8.For pultrusion and RTM

TK-107P	Reactive	0.30-0.50	6-12	65-71	50	3.0	120	80	High HDT, flame retardant, for FRP products, CCS approval
TK-1003	PA	0.35-0.55	7-10	59-65	48	1.2	170	90	Rigid, for producing fishing pole, tent pole, grille, etc
TK-2093	IPA	0.35-0.45	7-9	54-60	80	3.8	130	112	Heat and chemical resistance, for FRP products
TK-10200	PA	0.35-0.55	3-5.5	59-65	69	2.55	130	76	General purpose, for FRP pultrusion products
TK-1	PA	0.20-0.28	20-30	57-63	63	3.0	118	67	Low viscosity, pre-promoted, rapid wetting, for injection molding
TK-6007	PA	0.20-0.48	8-16	57-64	65	3.4	105	50	Low viscosity & shrinkage, easy operation for RTM
TK-21	PA	0.14-0.18	50-80	54-60	55	1.8	128	78	Pre-promoted, low PET, used in vacuum assisted resin injection molding

9. For FW pipe

Code	Type	25?  Pa.s Viscosity	Min gel time	% Non-Volatile	Mpa Tensile strength	% Elongation	Mpa Flexural Strength	HDT	Application
TK-102	IPA	0.20-0.40	7-13	51-57	64	2.0	115	105	For lining, good flexibility, chemical resistance and high HDT, for water supply and drainage pipe, petroleum pipe and chemical industry pipe, tank
TK-191FW	PA	0.30-0.50	15-30	60-67	65	2.5	120	81	For structure, flexible and good mechanical property for FW pipe and tanks
TK-1900	PA	0.30-0.40	30-35	62-68	65	2.5	120	70	For structure, low PET and crack resistance
TK-196SPFW	PA	0.30-0.50	8.5-17.5	60-68	70	2.0	120	70	For lining, to make FW pipe and tanks, food grade, CNH approval
TK-20820	IPA	0.22-0.48	9-21	58-64	72	3.2	120	86	For lining, to make FW pipe and tanks, food grade, CNH approval
TK-10600	PA	0.20-0.26	5-12	55-61	68	2.7	138	81	For structure and HOBAS pipe
TK-503831	PA	0.20-0.40	5.5-12.5	56-62	11	76			High elongation for lining and HOBAS pipe, food grade, CNH approval

10. For paint

TK-196YK	PA	0.70-1.10	10-18	64-70	76	2.0	120	72	Good surface smoothness, excellent chemical resistance, for piano, furniture etc, hand lay up
TK-196GZ	PA	0.30-0.50	10-18	59-65	74	1.8	125	75	Good surface smoothness, good workability, for curtain
TK-8001P	PA	S-U	7-13	54-60	62	2.5	120	75	Thixotropy, high hardness, for curtain
TK-8001S	PA	0.30-0.50	8-14	54-60	65	2.7	120	75	Thixotropy, high hardness, for spray up

11. For translucent panel

Code	Type	25?  Pa.s Viscosity	Min gel time	% Non-Volatile	Mpa Tensile strength	% Elongation	Mpa Flexural Strength	HDT	Application
TK-108	Reactive	0.25-0.55	30-60	62-69	62	2.8	123	56	Low viscosity and flame retardant
TK-10170	PA	0.13-0.25	7.5-14.5	54-60	56	1.8	115	73	Good light transmission and weather resistance, for hand lay up
TK-195	PA	0.12-0.24	28-56	58-64	55	1.2	115	54	Good light transmission and weather resistance, to make panels

12. Cultured marble


TK-1014	PA	0.30-0.40	4-8		65	3.0	120	56	Good transparency to casting crystal handcraft
TK-2006	IPA	0.30-0.45	5-9		76	4.2	120	72	Heat resistance, high elongation & impact strength, good workability for tabletop in kitchen
TK-10940	PA	1.25-1.80	4-11	67-71	55	6.2	103	60	Water & crack resistance, high elongation, for bath tub
TK-10950	PA	0.80-1.20	7-15	63-70	70	3.5	110	68	Good transparency and mechanical property
TK-1065	PA	0.60-0.80	12-25	66-71	68	1.8	106	90	Fast curing, good heat resistance and transparency for sanitary in bath room
TK-10140	PA	1.30-1.70	8-16		65	3	120	56	Excellent transparency to cast crystal handcraft

13. SMC/BMC


Code	Type	25?  Pa.s Viscosity	Min gel time	% Non-Volatile	Mpa Tensile strength	% Elongation	Mpa Flexural Strength	HDT	Application
TK-109	PA	1.5-2.0	9-18	67-73	65		93	91	General purpose, heat resistance, for production of SMC/BMC
TK-198	PA	0.45-0.80	11-20	60-67	60	1.4	115	100	General purpose, heat resistance, for production of SMC
TK-1008	PA	X-Z	3.5-6.5		57	2.13	96	135	High strength, low shrinkage, good surface, heat resistance, for production of SMC/BMC
TK-2006S	IPA	2.5-3.5	10-12	64-67	60	2.2	100	120	High strength, heat resistance, for production of electrical parts and sanitary ware
TK-5002	NPG	0.60-0.80	6-8	60-66	50	1.8	80	110	Glossy surface, heat resistance, for sanitary ware
TK-40094	PA	0.90-1.20	12-24	57-63	58	1.8	82	120	Weather resistance, heat & water resistance, for water tank, sanitary ware and auto parts

 

CHANGZHOU UTEK COMPOSITE COMPANY CO.,LTD
COMPANY INTRODUCTION:
Company Name	CHANGZHOU UTEK COMPOSITE CO.,LTD
Address	Fuhanyuan 1-814,Taihu Road,Changzhou,Jiangsu,China
Contact Person	Name		Tel		Email ID
Manger	Gong Xiaojun		0086 13357899376		gong@utekcomposite.com
Manger	Irene Xi		0086 13961156380		irene@utekcomposite.com
Business Condition	Manufacture			Trading
Consititution of company	Pvt.Ltd
Annual turnover	USD10,000,000
Company Occupy Areas(M2)	3000M2
Shower room Occupy Areas(M2)	200M2
website	www.utekcomposite.com
	http://utekcomposites.en.made-in-china.com/
Mainly Customer & Marketing	Europe,Asia,America,Middle East
Mainly Product	Fiberglass chopped strand mat (powder and emulsion), stitch mat, combo mat, uni-direction and biaxial fabric, RTM core mat, woven roving, special products like Ar-glass roving, chopped strand, thin fiberglass fabric, SMC(sheet molding compound), fiberglass/polyester geogrid and geocomposite. fiberglass mica fabric for insulation.
Sales Team	15(University Graduates)		Product Team		150
Research & Development Team	12		QC Team		8
Certificate	ISO 9001 ,ISO 14001 ,SGS
Give us a chance, and we' ll return you with satisfaction.